OSTAPLAST RED 2G

Characteristic
C. I. Solvent Red 111
C. I. No. 60505
CAS No. 82-38-2
Chemical Class Anthraquinone
 
Illustrations
       
Red 2g 0,01 %
Red 2g 0,05 %
Red 2g 0,10 %
Red 2g 0,10 % + TiO2
0,01 % 0,05 % 0,10 % 0,10 % + TiO2

 

Properties
Specific Weight [g/cm3] 1,35
Bulking Volume [ l/kg] 11
Melting Point [°C] 170
Concentration for 1/3 of Standard Depth in PS [%] 0,251

 

Fastness to Chemicals
  Resistance to radical forming agents
Dibenzoyl-peroxide +
Methyl-ethyl-keton-peroxide +
Dilauroyl-peroxide +
  Fastness to bleeding in PS
Destilled Water 5
5 % Acetic Acid 5
15 % ethanol 5
Cooking oil 5
50 % ethanol 5
n-heptan 5
3 % Solution Na2CO3 in Water 5
Solution 2 % NaCl and 2 % Wine Acid 5
  Other Fastness
Light - full shade - 0,05 % 7
Light - 0,05% + 1% TiO2 6
Heat Resistance [°C] 300
Migration 5

 

Curves
Transmission Curve
Transmission Curve-RED 2G
Remission Curve
Remission Curve-RED 2G

 

 

Application Possibilities  
Polystyrene
suitable
ABS
suitable
Polycarbonate
suitable
PA 6
unsuitable
PA 6,6
unsuitable
Polyethylenterephtalate
unsuitable
suitable partially suitable
 
Testing methods
  • Specific weight - Was determined by automatic gas pycnometer in g/cm3
  • Bulking volume - Denotes the volume of 1 kg loosely poured dye, expressed in litres
  • Melting point [°C] - Was determined by DSC method (Differencial Scanning Calorimeter)
  • Concentration for 1/3 of standard    depth - Concentration of the dye in % for coloring of polystyrene containing      1% TiO2 to get 1/3 of standard depth
  • Transmission curve - Graphic image of dependence of transmission on wave length measured    on chips made of polystyrene Krasten 127 with the thickness of 2 mm and    content of dyestuff of 0,01 %
  • Reflection curve - Graphic image of dependence of reflection on wave length measured on    chips made of polystyrene Krasten 127 with the content of dyestuff of 0,01 %    and 1 % TiO2.
  • Fastness to bleeding - Testing was done according to Resolution AP(89) 1 (Council of Europe    Commitee of Ministers) for using of colourants in plastic materials comming    into contact with food. Chips made of polystyrene Krasten 127 with content of    0,1 % of dyestuffs was in contact with food-simulating liquids for 5 hours at    50 °C. Bleeding (staining of liquids) was assessed using 5 degree Intemational    Grey Scale ISO 105 A2 where 5 indicates no bleeding
  • Resistance to radical-forming agents - Polyester resin Aropol FS-9945 with content of 0,05 % dyestuff was    cured 30 minutes at 80 °C using addition of 2 % hardening agent. The change of    color shade after curing was asessed in comparisson with the colour of the    solution of dyestuffs in the resin before curing.
    + the dye is suitable (without colour change)
    - the dye is not suitable (heavy colour change)
  • Light fastness - Xenotest - ČSN EN ISO 105 B02:2000. Determined according to blue    scale, by it degree 1 denotes the lowest fastness, degree 8 the highest one
    A - Full Shade 0,05 % in PS
    B - 0,05 % + 1 % Ti02 in PS
  • Heat Resistance - Was determined by injection moulding machine over the    temperature range 200 - 300°C Moldings were prepared after 5 minutes dwell    time at each test temperature and were compared against control moulding    prepared at the lowest test temperature - 180 °C (dyeing 0,1 % + 1 % TiO2 in PS Krasten 127)
  • Migration - Tested by placing a chips of coloured    PS in contact with a sample of PS containing only 1 % TiO2 for 1    day at 70°C. Any stain was assested using ISO Grey Scale, where 5 indicates no    stain.
Detailed product information can also be saved in PDF format    PDF